Dynamic Strain Ageing During Stress Relaxation in Selected Magnesium Alloys Containing Rare earth Elements

Abstract Three magnesium alloys containing rare earth were deformed at room temperature and above room temperature at various strain rates. Stress relaxation tests were performed in order to study dynamic strain ageing phenomena effects. Different manifestations of strain ageing were observed. Non‐monotonous temperature and strain rate dependence of the flow stress were observed. Post relaxation effect, i.e. an increase of the flow stress at the beginning of plastic deformation after stress relaxation in comparison to the flow stress at the beginning of stress relaxation, was detected.

۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲. ۲

چکیده سه آلیاژ منیزیم حاوی زمین نادر در دمای اتاق و دمای اتاق در نرخ‌های کرنش مختلف تغییر شکل می‌دهند. آزمون‌های آرامش استرس به منظور مطالعه اثرات پدیده پیری بر پدیده پیری انجام شد. تظاهرات مختلف پیری ناشی از کرنش مشاهده شد. دمای غیر یکنواخت و وابستگی نرخ کرنش به تنش سیلان مشاهده شد. اثر شل پس از تنش، یعنی افزایش تنش سیلان در شروع تغییر شکل پلاستیک پس از تنش جریان در مقایسه با تنش سیلان در آغاز تنش ملایم، شناسایی شد.
ترجمه شده با


پر ارجاع‌ترین مقالات مرتبط:

  • مقاله General Materials Science
  • ترجمه مقاله General Materials Science
  • مقاله علوم مواد عمومی
  • ترجمه مقاله علوم مواد عمومی
  • مقاله Condensed Matter Physics
  • ترجمه مقاله Condensed Matter Physics
  • مقاله فیزیک ماده چگال
  • ترجمه مقاله فیزیک ماده چگال
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.