Effect of silica filler on dynamic mechanical properties of lonic elastomer based on carboxylated nitrile rubber

Abstract Variation of dynamic mechanical propeties like storage modulus (E′) and loss tangent (tan δ) with temperature show the presence of two transitions in the carboxylated nitrile rubber (XNBR) molded in the presence of zinc oxide (ZnO). The low‐temperature transition is due to the glass–rubber transition (Tg) of XNBR, and the high‐temperature transition is due to formation of ionic clusters. Incorporation of reinforcing silica filler makes the high temperature transition more prominent and high filler loading casues a shift of the transition temperature to the higer side. It is believed that the rubber–filler interaction in the cluster region causes striking changes in the variation of E′ and tan δ with a double‐strain amplitude (DSA). © 1995 John Wiley & Sons, Inc.

اثر پرکننده سیلیکا بر خواص مکانیکی دینامیکی الاستومر lonic بر روی لاستیک نیتریل

چکیده تنوع خواص مکانیکی پویا مثل مدول ذخیره (E)و تانژانت داخلی (tan δ)با دما حضور دو گذار در لاستیک نیتریل (XNBR)را نشان می‌دهد که در حضور اکسید روی (ZnO)شکل گرفته‌اند. انتقال کم دما ناشی از انتقال لاستیک - (Tg)XNBR است و گذار با دمای بالا ناشی از تشکیل خوشه‌های یونی است. الحاق پرکننده سیلیکا باعث می‌شود که انتقال حرارت بالا به بالا و بار پر کننده بالا منجر به تغییر دمای انتقال به سمت چپ شود. اعتقاد بر این است که تعامل پر کننده لاستیک در منطقه خوشه باعث ایجاد تغییرات قابل‌توجه در تغییر شکل E و برنزه شدن با دامنه فشار مضاعف (DSA)می‌شود. ۱۹۹۵ جان ویلی، پسران، شرکت Inc.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.