The plasticization of an epoxy resin by dibutylphthalate and water

Abstract The glass‐transition temperature of an epoxy resin cured at two different temperatures and plasticized with water and dibutylphthalate has been studied. Both modulus of elasticity and yield stress were measured as a function of temperature to determine the glass‐transition temperature. Drying a saturated material appeared to restore the glass‐transition temperature to its original value but some broadening of the transition occurred. The behavior of an undercured epoxy when saturated with water could not be predicted by theory. A substantial increase in the transition temperature was observed which may have been caused by the presence of water and an expanded structure.

نرم‌کننده رزین اپوکسی با دی بوتیل فتالات و آب

چکیده دمای انتقال شیشه‌ای یک رزین اپوکسی پخت شده در دو دمای مختلف و نرم شوندگی با آب و دی بوتیل فتالات مورد مطالعه قرار گرفته‌است. هم مدول الاستیسیته و هم تنش تسلیم به عنوان تابعی از دما برای تعیین دمای انتقال شیشه‌ای اندازه‌گیری شدند. به نظر می‌رسد که خشک کردن یک ماده اشباع، دمای انتقال شیشه‌ای را به مقدار اصلی خود باز می‌گرداند، اما مقداری گسترش انتقال رخ می‌دهد. رفتار یک اپوکسی پخت نشده وقتی که با آب اشباع شده‌باشد را نمی توان با تئوری پیش‌بینی کرد. یک افزایش قابل‌توجه در دمای گذار مشاهده شد که ممکن است ناشی از حضور آب و یک ساختار گسترده باشد.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.