A Partial Isothermal Section at 1000 °C of Al-Mn-Fe Phase Diagram in Vicinity of Taylor Phase and Decagonal Quasicrystal

Altogether 19 alloys of an Al-Mn-Fe system with compositions near to the Taylor phase and/or the decagonal quasicrystal were characterised by the x-ray diffraction and the energy-dispersive x-ray spectroscopy coupled with the scanning electron microscopy, after annealing at 1000 °C for 330 h. The obtained experimental results were used to propose a partial isothermal section at 1000 °C of the Al-Mn-Fe phase diagram. The ternary T-phase area of an untypical saddle shape was found to touch the Al-Mn binary one. The γ 2 -phase was found to be stable between 2 and 30 at.% of Fe at 1000 °C and boundaries between γ 1 - and γ 2 -areas are expected to be located very close to the Al-Mn binary.

بخش Isothermal جزیی در ۱۰۰۰ ° C از نمودار فاز Fe - Fe - Fe - Fe - Fe در فاز تیلور و Decagonal Quasicrystal

روی هم رفته ۱۹ آلیاژهای یک سیستم سانتافه با ترکیبات نزدیک به فاز تیلور و / یا the decagonal با پراش اشعه ایکس و طیف‌سنجی پراش پرتو ایکس همراه با میکروسکوپ الکترونی اسکن بعد از تابکاری در ۱۰۰۰ درجه سانتی گراد به مدت ۳۳۰ ساعت مشخص شدند. نتایج تجربی به‌دست‌آمده برای ارایه یک بخش ایزوترمال و ایزوترمال در دمای ۱۰۰۰ درجه سانتی گراد از نمودار فاز Al - منگنز استفاده شد. شکل سه فازی سه فازی یک زین untypical برای تماس با Mn دوتایی Al یافت شد. فاز γ ۲ - ۲ ثابت شد که بین ۲ تا ۳۰ اینچ ثابت است. انتظار می‌رود که % % Fe در دمای ۱۰۰۰ درجه سانتی گراد و فاصله بین γ ۱ و γ ۲ - γ در نزدیکی to - قرار داشته باشند.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.