Properties of 3D-Printed Fiber-Reinforced Portland Cement Paste

In this chapter, insight into an automatically 3D-printed composite of Portland cement paste and reinforcing short fibers (carbon, glass and basalt fibers, 3–6 mm) are presented, resulting in novel materials that exhibit high flexural (up to 30 MPa) and compressive strength (up to 80 MPa). Previous tests with a manual nozzle-injection method suggest a potential flexural strength of up to 120 MPa. Alignment of the fibers caused by the 3D-printing process is observed, opening up the possibility to use the print path direction as a means to control fiber orientation within the printed structures. Apart from completely dense cementitious bodies, hierarchically structured bodies displaying precisely adjusted macroporosity are presented, the latter exhibiting a unique combination of strength and materials efficiency.

چسباندن چسباندن سیمان پورتلند ۳ D - چاپی

در این فصل، بینش به یک کامپوزیت به طور خودکار سه‌بعدی از خمیر سیمان پورتلند و تقویت‌کننده فیبرهای کوتاه (کربن، شیشه و الیاف بازالت، ۳ تا ۶ mm)ارائه می‌شود که منجر به موادی جدید می‌شود که خمشی بالایی (تا ۳۰ MPa)و مقاومت فشاری (تا ۸۰ MPa)نشان می‌دهند. آزمایش‌های قبلی با روش تزریق nozzle دستی، یک قدرت موجی بالقوه را تا ۱۲۰ MPa نشان می‌دهد. ردیف کردن الیاف ناشی از فرآیند چاپ سه‌بعدی مشاهده می‌شود که امکان استفاده از جهت مسیر چاپ را به عنوان وسیله‌ای برای کنترل جهت گیری الیاف در ساختارهای چاپی فراهم می‌کند. علاوه بر بدنه‌های سیمانی کاملا متراکم، بدنه‌های ساخت یافته به صورت سلسله مراتبی نشان داده می‌شوند که به طور دقیق تنظیم‌شده و ترکیب منحصر به فرد از قدرت و کارایی مواد را نشان می‌دهد.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.