Polymorphism in polyamide 66/clay nanocomposites

Polyamide 66/clay nanocomposites (PA66CN) were prepared via melt compounding method by using a new kind of organophilic clay, which was obtained through co-intercalation of epoxy resin and quaternary ammonium into Na-montmorillonite. The silicate layers were dispersed homogeneously and nearly exfoliated in polyamide 66 (PA66) matrix. The introduction of silicate layers induced the appearance of the γ phase in PA66CN at room temperature, more clay loadings would amplify this phenomenon; the addition of clay also changed the structure of the α crystalline phase. The presence of silicate layers increased the crystallization rate and had a strong hetero phase nucleation effect on PA66 matrix. The lower Brill transition temperature of PA66CN can be attributed to the strong interaction between polyamide chains and surfaces of silicate layers.

پلی مورفیسم در نانوکامپوزیت های پلی‌آمید ۶۶ / خاک رس

نانوکامپوزیت های پلی‌آمید ۶۶ / خاک رس (PA۶۶CN)از طریق روش ترکیب مذاب با استفاده از نوع جدیدی از خاک رس ارگانیک تهیه شدند که از طریق اتصال مشترک رزین اپوکسی و آمونیوم چهارتایی به مونت موریلونیت - Na به دست آمد. لایه‌های سیلیکات به صورت همگن و تقریبا در ماتریس پلی‌آمید ۶۶ (PA۶۶)پراکنده شدند. معرفی لایه‌های سیلیکاتی ظهور فاز γ در PA۶۶CN در دمای اتاق را القا می‌کند، بارگذاری‌های بیشتر رس این پدیده را تقویت می‌کند؛ افزودن رس همچنین ساختار فاز بلوری α را تغییر می‌دهد. حضور لایه‌های سیلیکاتی نرخ تبلور را افزایش داد و اثر هسته زایی فاز هتروژنی قوی بر ماتریس PA۶۶ داشت. دمای پایین‌تر انتقال بریل PA۶۶CN می‌تواند به اثر متقابل قوی بین زنجیره‌های پلی‌آمید و سطوح لایه‌های سیلیکاتی نسبت داده شود.
ترجمه شده با

سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.