Reinforcing 316L stainless steel with intermetallic and carbide particles

A study was made of the change in properties of 316L stainless steel depending on the type and the amount of added reinforcement. The reinforcements used were Cr2Al, Cr2Ti, VC, SiC; and the amounts were 1.5 and 3 vol.%. All materials were manufactured by mixing the powders with 0.6 wt.% of wax, compacting at 700 MPa, and sintering at 1230 °C in a 75% H2–25% N2 atmosphere. The properties evaluated include sintering density, tensile strength, hardness, corrosion (salt spray test) and wear, and a microstructural study was also made. The intermetallics and carbides mostly improve corrosion properties without degrading mechanical properties.

تقویت فولاد ضد زنگ ۳۱۶ L با ذرات بین فلزی و کاربیدی

یک مطالعه از تغییر در خواص فولاد ضدزنگ ۳۱۶ L بسته به نوع و مقدار تقویت اضافه‌شده انجام شده‌است. تقویت‌کننده‌های مورد استفاده Cr۲Al، Cr۲Ti، VC، SiC بودند؛ و مقادیر ۱.۵ و ۳ حجمی بودند. %. همه مواد با مخلوط کردن پودرها با wt. % موم، در فشار ۷۰۰ مگاپاسکال فشرده می‌شود و در دمای ۱۲۳۰ درجه سانتیگراد در اتمسفر ۷۵ % H۲ - ۲۵ % N۲ سینتر می‌شود. خواص مورد ارزیابی شامل چگالی سینتر، استحکام کششی، سختی، خوردگی (تست اسپری نمک)و فرسایش، و یک مطالعه ریزساختاری نیز ساخته شد. ترکیبات بین فلزی و کاربیدها عمدتا خواص خوردگی را بدون کاهش خواص مکانیکی بهبود می‌بخشند.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.