Combined effect of isothermal annealing and pre-compression on mechanical properties of Cu36Zr48Al8Ag8 bulk metallic glass

The combined effects of isothermal annealing and pre-compression on the mechanical properties of Cu36Zr48Al8Ag8 bulk metallic glass (BMG) were investigated. The as-cast specimens were first annealed at 743 K for 10 min, and then pre-compressed under 800 MPa for 1, 3, 5 and 10 h, respectively. The results indicated that annealing resulted in the formation of nanocrystals with a diameter of ~10 nm in the amorphous matrix and a drastic decrease of the free volume, leading to complete loss of the plasticity of the BMG. Applying pre-compression under a stress of 800 MPa for a proper duration (5 h) resumed part of the lost free volume in the BMG matrix and therefore partially recovered the plasticity. A very long period of pre-compression (10 h) decreased the free volume again, which was caused by the excessive crystal growth.

اثر ترکیبی تابکاری هم دما و پیش فشاری بر خواص مکانیکی شیشه فلزی Cu۳۶Zr۴۸Al۸Ag۸

اثرات ترکیبی تابکاری هم دما و پیش فشاری بر خواص مکانیکی شیشه فلزی مخصوص ظاهری (BMG)مورد بررسی قرار گرفت. نمونه‌های ریخته‌گری شده ابتدا در ۷۴۳ K به مدت ۱۰ دقیقه آنیل شدند و سپس تحت فشار ۸۰۰ مگاپاسکال به ترتیب برای ۱، ۳، ۵ و ۱۰ ساعت قرار گرفتند. نتایج نشان داد که تابکاری منجر به تشکیل of با قطر ۱۰ nm در زمینه آمورف و کاهش شدید حجم آزاد می‌شود که منجر به از دست رفتن کامل پلاستیسیته the می‌شود. اعمال فشار قبل از فشردگی تحت فشار ۸۰۰ مگاپاسکال برای مدت مناسب (۵ ساعت)بخشی از حجم خالی از دست رفته در ماتریس BMG را ازسر گرفت و بنابراین به طور نسبی پلاستیسیته را بهبود بخشید. یک دوره بسیار طولانی از پیش - فشرده‌سازی (۱۰ ساعت)دوباره حجم آزاد را کاهش داد، که ناشی از رشد بلور بیش از حد بود.
ترجمه شده با

سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.