Degradation of passive film on 304 stainless steel in a simulated concrete pore solution under alternating temperature condition

For simulating the performance of stainless steel reinforcement under temperature change in the tropical environment, passive behavior of 304 stainless steels was studied in the pore solutions under alternating-temperature condition. The results suggested that the passive films were more severely degraded under the higher frequency or the larger amplitude of temperature alternation. Local breakdown of passive film and cracks occurred in the films as the samples experienced the low amplitude and the high amplitude of temperature alternation, respectively. Furthermore, the rupture initially started in the inner Cr2O3 layer and then propagated into the outer iron oxides layer.

تخریب فیلم پسیو بر روی فولاد ضدزنگ ۳۰۴ در محلول حفره‌های بتون شبیه‌سازی شده تحت شرایط دمای متناوب

برای شبیه‌سازی عملکرد تقویت فولاد ضد زنگ تحت تغییر دما در محیط گرمسیری، رفتار غیر فعال فولاد ضد زنگ ۳۰۴ در محلول‌های منفذ تحت شرایط دمای متناوب مطالعه شد. نتایج نشان داد که لایه‌های پاسیو تحت فرکانس بالاتر یا دامنه تغییرات دما به شدت تخریب می‌شوند. هنگامی که نمونه‌ها به ترتیب دامنه کم و دامنه زیاد تناوب دما را تجربه کردند، شکست موضعی لایه پاسیو و ترک‌ها در لایه‌ها رخ داد. علاوه بر این، در ابتدا گسیختگی در لایه داخلی شروع شد و سپس در لایه اکسید آهن بیرونی تکثیر شد.
ترجمه شده با


پر ارجاع‌ترین مقالات مرتبط:

  • مقاله General Materials Science
  • ترجمه مقاله General Materials Science
  • مقاله علوم مواد عمومی
  • ترجمه مقاله علوم مواد عمومی
  • مقاله Building and Construction
  • ترجمه مقاله Building and Construction
  • مقاله ساختمان‌سازی و ساخت و ساز
  • ترجمه مقاله ساختمان‌سازی و ساخت و ساز
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.