Morphology and microstructure of ZrB2–SiC ceramics after ablation at 3000 oC by oxy-acetylene torch

Application of ZrB2–SiC ceramic at temperatures above 2500 °C requires evaluation of the ablation behavior of the material. The ZrB2–SiC ceramics with SiC contents of 15% and 30% in volume were fabricated by SPS under a temperature of 1580 °C. The ceramics were then ablated by an oxy-acetylene flame with a temperature of 3000 °C. It was found that ZrB2–SiC consists of three distinct ablation layers (ZrO2, SiO2-rich, and SiC-depleted) after ablation. The ablation mechanism revealed that ZrB2–SiC forms a SiO2-rich layer, which slows down the diffusion of oxygen but accelerates the active oxidation of SiC.

ریخت‌شناسی و ریزساختار سرامیک ZrB۲ - SiC بعد از سوزاندن در دمای ۳۰۰۰ درجه سانتیگراد با استفاده از مشعل اکسی استیلن

کاربرد سرامیک ZrB۲ - SiC در دمای بالای ۲۵۰۰ درجه سانتیگراد نیاز به ارزیابی رفتار ablation مواد دارد. سرامیک‌های ZrB۲ - SiC با محتوای SiC ۱۵ % و ۳۰ % در حجم توسط SPS تحت دمای ۱۵۸۰ ° C ساخته شدند. سپس سرامیک توسط یک شعله اکسی استیلن با دمای ۳۰۰۰ درجه سانتی گراد ablated شدند. مشخص شد که ZrB۲ - SiC متشکل از سه لایه ablation مجزا (ZrO۲، SiO۲ - غنی و SiC - depleted)بعد از سوزاندن است. مکانیسم ablation نشان داد که ZrB۲ - SiC یک لایه غنی از SiO [ ۲ ] را تشکیل می‌دهد، که نفوذ اکسیژن را کاهش می‌دهد اما اکسیداسیون فعال of را تسریع می‌کند.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.