Stress intensity solutions of thermal fatigue induced cracks in a thin plate hot spot using LEFM and finite element analysis

The chief aim of this research is to marry elegant LEFM methods, published material data, and a commercially available FEA code together to represent complex crack growth and arrest phenomena in a thin plate with residual viscoplastic stresses. Additionally, representing the variation in these stress intensities across a thermal gradient to include ultimate fatigue crack arrest is of specific interest. To the authors’ knowledge, modeling fracture mechanics due to these hot spots with viscoplastic residual stresses using LEFM methods on this type structure has not been achieved. With these stress intensities, predictions are to be made regarding not only the FCG rate but the probable radial arrest distance of a nominal crack from the hot spot center.

فشار استرس ناشی از خستگی حرارتی باعث ایجاد ترک‌های ناشی از خستگی گرمایی در یک نقطه داغ با استفاده از آنالیز آلمان محدود و محدود می‌شود.

هدف اصلی این پژوهش، ازدواج با روش‌های elegant، انتشار داده‌های مادی، و یک کد FEA موجود تجاری برای نمایش رشد ترک پیچیده و پدیده بازداشت در یک صفحه نازک با تنش‌های پسماند جامد می‌باشد. علاوه بر این، نشان دادن تنوع در این شدت‌های استرس در یک گرادیان حرارتی تا شامل مقاومت نهایی ترک خستگی خاص است. با توجه به دانش نویسندگان، مدل‌سازی مکانیک شکست با توجه به این نقاط داغ با تنش‌های پسماند جامد و ویسکوپلاستیک با استفاده از روش‌های LEFM بر روی این نوع ساختار به دست نیامده است. با این شدت فشار، پیش‌بینی‌ها با توجه به نرخ FCG نه تنها فاصله کانونی احتمالی یک ترک اسمی از مرکز نقطه داغ ساخته می‌شوند.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.