Enhanced microhardness in nanocomposite Ti60Cu14Ni12Sn4Ta10 processed by high pressure torsion

Nanostructured Ti60Cu14Ni12Sn4Ta10 alloys have been obtained by (i) arc-melting (AM) the pure elements and (ii) AM followed by severe plastic deformation induced by high pressure torsion (HPT). Scanning electron microscopy (SEM) reveals that the AM specimen consists of a dendrite–eutectic structure. After the HPT, the center of the disks exhibits a microstructure similar to the AM specimen but with strongly deformed dendrites and the lamellae become refined and intermixed as the distance from the disk center increases. At the edge of the HPT disks the dendritic/eutectic morphology is no longer observed by SEM. The Vickers microhardness is higher in the HPT disks as compared to the AM samples. This result is discussed in terms of the peculiar morphologies and nanostructures achieved after each processing route.

افزایش سختی در نانوکامپوزیت به وسیله فرآیند پیچش با فشار بالا پردازش می‌شود.

آلیاژهای nanostructured Ti۶۰Cu۱۴Ni۱۲Sn۴Ta۱۰ از طریق ذوب قوس (AM)عناصر خالص و (II)با تغییر شکل پلاستیک شدید ناشی از پیچش با فشار بالا (hpt)به دست آمده‌اند. میکروسکوپ اسکن الکترونی (SEM)نشان می‌دهد که نمونه AM شامل یک ساختار dendrite - اوتکتیک است. بعد از the، مرکز دیسک‌ها یک ریز ساختار مشابه به نمونه AM نشان می‌دهد اما دارای دندریت قوی تغییر شکل و لایه lamellae با افزایش فاصله مرکز دیسک اصلاح‌شده و intermixed می‌شود. در لبه disks hpt / morphology dendritic / اوتکتیک دیگر توسط SEM مشاهده نمی‌شود. سختی ویکرز در دیسک‌های hpt نسبت به نمونه‌های AM بیشتر است. این نتیجه در مورد مورفولوژی خاص و نانوساختارها مورد بحث قرار می‌گیرد که بعد از هر مسیر پردازش بدست‌آمده است.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.