Hydrothermal synthesis of Na2Ti6O13 and TiO2 whiskers

Na2TinO2n+1 typed whiskers has been extensively used for frictional materials, reinforcement materials and high insulators, and TiO2 whiskers can be applied for catalyst support and photocatalysts. Na2Ti6O13 whiskers were easily synthesized by hydrothermal treatment of the mixed solution of spherical TiO2 powder with anatase structure and NaOH solution at 250 °C for 4 h. The sodium titanate (Na2Ti6O13) whiskers obtained had a smooth surface and high aspect ratio of 100 nm below in diameter and 100 μm above in length. TiO2 whiskers were obtained by acid treatment of the Na2Ti6O13 whiskers in 0.5 M HCl solution at 100 °C for 48 h. This suggests that Na ions in the Na2Ti6O13 structure were extracted during acid treatment and the formed TiO2·nH2O hydrate was turned to the TiO2 whisker with anatase phase.

سنتز هیدروترمال ویسکرهای Na۲Ti۶O۱۳ و TiO۲

ویسکرهای تایپ شده به طور گسترده برای مواد اصطکاکی، مواد تقویتی و عایق‌های بلند استفاده شده‌اند، و ویسکرهای TiO۲ را می توان برای پشتیبانی کاتالیزور و فتوکاتالیست به کار برد. ویسکرهای Na۲Ti۶O۱۳ به راحتی توسط عملیات هیدروترمال محلول مخلوط پودر TiO۲ کروی با ساختار آناتاز و محلول NaOH در دمای ۲۵۰ درجه سانتی گراد به مدت ۴ ساعت سنتز شدند. ویسکرهای سدیم تیتانات (Na۲Ti۶O۱۳)به‌دست‌آمده دارای سطح صاف و نسبت ابعاد بالای ۱۰۰ نانومتر زیر قطر و ۱۰۰ میکرومتر بالای طول بودند. ویسکرهای TiO۲ با تیمار اسیدی ویسکرهای Na۲Ti۶O۱۳ در محلول HCl ۰.۵ M در دمای ۱۰۰ درجه سانتی گراد به مدت ۴۸ ساعت به دست آمدند. این نشان می‌دهد که یون‌های Na در ساختار Na۲Ti۶O۱۳ در طول عملیات اسیدی استخراج شدند و TiO۲ nهیدرات شکل‌گرفته به ویسکر TiO۲ با فاز آناتاز تبدیل شد.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.