Effect of heat treatment of carbon nanofibers on polypropylene nanocomposites

Carbon nanofibers (CNFs) synthesized at 600 °C were modified at thermal treatment temperatures of 1200, 1800, and 2200 °C. These CNFs were incorporated into polypropylene (PP) at 10 wt% level by intensive mixing. Volume resistivity of composites containing CNFs heat treated at 2200 °C was higher than that of composites containing untreated CNFs. BET adsorption isotherms showed a significant reduction of specific surface area of CNFs after heat treatment, resulting from the decrease of pore volume without a change of surface roughness. In addition, scanning electron microscopy (SEM) micrographs revealed that after mixing, heat treated CNFs had a narrower length distribution (1–10 μm) than that of untreated CNFs (1–30 μm). We believe that these morphological changes of CNFs due to heat treatment contribute to a higher resistivity of composites with CNFs possessing even more graphitic content.

اثر تیمار گرمایی نانوالیاف به پلی پروپیلن در نانوکامپوزیت پلی پروپیلن

نانوالیاف کربنی (CNFs)که در دمای ۶۰۰ ° C سنتز شد در دماهای عمل‌آوری گرمایی ۱۲۰۰، ۱۸۰۰ و ۲۲۰۰ درجه سانتی گراد اصلاح شد. این CNF در پلی پروپیلن (PP)در ۱۰ درصد وزنی با اختلاط شدید ترکیب شد. مقاومت حجم کامپوزیتهای حاوی فیبر CNFs در دمای ۲۲۰۰ درجه سانتی گراد بیشتر از کامپوزیت حاوی CNF است. isotherms BET با کاهش قابل‌توجهی از ناحیه ویژه CNF را بعد از تیمار حرارتی نشان داد که ناشی از کاهش حجم حفرات بدون تغییر زبری سطح است. تجزیه و تحلیل میکروسکوپ الکترونی نشان داد که بعد از مخلوط کردن CNF، CNT نسبت به CNF ((۱ تا ۳۰ میکرومتر)توزیع شد. ما باور داریم که این تغییرات مورفولوژیک CNFs نسبت به CNT نسبت به CNT، نسبت به CNT ها بیشتر است.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.