Effects of Ca and Al on microstructural and tribological behavior of Mg-Al-Ca ternary alloy

The use of magnesium and its alloy is increased in biomedical and automobile applications with advantages of higher strength to weight ratio and good biocompatibility. In the present work, the effect of addition of Calcium on microstructural and tribological behaviour have been studied. In Mg-Al-Ca ternary system, alloying element amount were varied i.e. Ca in the range of 1%-6% and Al in the range of 3%-8%. For uniform distribution of phases, alloying has been done by stir casting with atmosphere controlled furnace. The microstructure analysis were carried out by optical microscopy to study the intermetallic compounds formed during solidification along with wear study performed on pin-on-disc tribometer. Wear analysis showed that addition of Ca improved the wear resistance due to formation of stable compounds of Mg2Ca and (Mg, Al)2Ca intermetallic phases.

اثرات Ca و Al بر ریزساختار و رفتار تریبولوژیکی آلیاژ سه تایی Mg - Al - Ca

استفاده از منیزیم و آلیاژ آن در کاربردهای پزشکی و خودرو با مزایای نسبت استحکام به وزن بالاتر و زیست سازگاری خوب افزایش می‌یابد. در کار حاضر، تاثیر افزودن کلسیم بر روی ریز ساختار و رفتار تریبولوژیکی مورد مطالعه قرار گرفته‌است. در سیستم سه تایی Mg - Al - Ca، مقدار عناصر آلیاژی متفاوت بود یعنی Ca در محدوده ۱ % - ۶ % و Al در محدوده ۳ % - ۸ %. برای توزیع یکنواخت فازها، آلیاژسازی با ریخته‌گری هم‌زنی با کوره کنترل‌شده با اتمسفر انجام شده‌است. آنالیز ریز ساختار با میکروسکوپ نوری برای مطالعه ترکیبات بین فلزی تشکیل‌شده در طول انجماد همراه با مطالعه فرسایش انجام‌شده بر روی تریبومتر پین روی دیسک انجام شد. آنالیز فرسایش نشان داد که افزودن Ca مقاومت سایشی را به دلیل تشکیل ترکیبات پایدار Mg۲Ca و فازه‌ای بین فلزی (Mg، Al)۲ Ca بهبود می‌بخشد.
ترجمه شده با

سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.