Tensile, hardness and microstructural properties of Sn-Pb solder alloys

This work investigated the Tensile, Hardness and Microstructural Properties of Sn-Pb Solder Alloys of Pb content 15, 60 and 80%. The Sn-Pb solder alloy was prepared from granulated Sn and Pb. The element was mixed in right proportions, melted in furnace at 350 °C while being held in crucible. The results showed that maximum tensile stresses obtained had specimen containing 60% with the highest value and the alloys had decreased hardness as a result of increased Pb content while ductility of the alloy increased as observed from stress strain curve. The sample alloy with 60% Pb is the preferred solder.

خواص کششی، سختی و ریزساختاری آلیاژهای لحیم Sn - Pb

این کار خواص کششی، سختی و ریزساختاری Sn - Pb Sold Alloys از Pb محتوای ۱۵، ۶۰ و ۸۰ % را مورد بررسی قرار داد. آلیاژ لحیم Sn - Pb از Sn و Pb گرانوله شده آماده شد. عنصر به نسبت‌های درست مخلوط شد، در کوره در دمای ۳۵۰ درجه سانتی گراد ذوب شد در حالی که در صلیب نگه‌داشته می‌شد. نتایج نشان داد که حداکثر تنش کششی بدست‌آمده دارای نمونه‌ای حاوی ۶۰ % با بالاترین مقدار بود و آلیاژها سختی را در نتیجه افزایش مقدار Pb کاهش دادند در حالی که انعطاف‌پذیری آلیاژ با مشاهده منحنی کرنش تنش افزایش یافت. آلیاژ نمونه با ۶۰ % Pb لحیم ارجح است.
ترجمه شده با

سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.