Effect of oxygen concentration upon the ductility of amorphous Zr57Nb5Al10Cu15.4Ni12.6

The effect of oxygen content on the mechanical and thermal properties of Zr57Nb5Al10Cu15.4Ni12.6 bulk metallic glass was measured. Oxygen was systematically added to a master alloy through the addition of ZrO2. Compression, Vickers hardness and bending, differential scanning calorimetry (DSC) and X-ray measurements were performed. Material with no additional oxygen demonstrated the ability to deform through multiple shear band formation, while that with higher oxygen content retained up to 90% of its compressive strength but lost virtually all ductility. The loss of ductility is attributed to the formation of Zr2Cu- and Zr2Ni-type intermetallic oxide particles.

اثر غلظت اکسیژن در شکل‌پذیری of آمورف. ۴ Ni۱۲. ۶

تاثیر محتوای اکسیژن بر خواص مکانیکی و حرارتی of. ۴ Ni۱۲. ۶ شیشه فلزی عمده اندازه‌گیری شد. اکسیژن به طور سیستماتیک به یک آلیاژ با اضافه کردن ZrO۲ اضافه شد. فشرده‌سازی، سختی ویکرز و خمشی، گرماسنجی روبشی تفاضلی (DSC)و اندازه‌گیری‌های اشعه ایکس انجام شد. مواد بدون اکسیژن اضافی توانایی شکل کردن از طریق تشکیل یک گروه برشی چندگانه را نشان دادند، در حالی که مقدار اکسیژن بالاتر تا ۹۰ % از مقاومت فشاری خود را حفظ کرده، اما تقریبا همه ductility را از دست داد. از دست دادن of به تشکیل ذرات اکسید Zr۲Cu - و Zr۲Ni - type منسوب است.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.