Role of elastostatic loading and cyclic cryogenic treatment on relaxation behavior of Ce-based amorphous alloy

In this work, Ce65Cu15Al10Ni8Co2 bulk metallic glass was annealed at sub-Tg and then elastostatically and cryogenically was loaded and treated, respectively. X-ray Diffraction (XRD) analysis was carried out to show amorphousness of treated alloys, and enthalpy variations and specific heat capacity were evaluated using differential scanning calorimetry (DSC). The results showed that the designed treatment procedure leads to the recovery of relaxation, i.e. rejuvenation, from the relaxed state to the as-cast condition. It is suggested that the generation of free volume and the structural rearrangements, appeared in the abnormal behavior of DSC curves, are responsible for recovery of relaxation. It is also found that the primary elastostatic loading facilitates the subsequent rejuvenation evolution caused by the cryogenic cycling process.


پر ارجاع‌ترین مقالات مرتبط:

  • مقاله General Materials Science
  • ترجمه مقاله General Materials Science
  • مقاله علوم مواد عمومی
  • ترجمه مقاله علوم مواد عمومی
  • مقاله Mechanics of Materials
  • ترجمه مقاله Mechanics of Materials
  • مقاله مکانیک مواد
  • ترجمه مقاله مکانیک مواد
  • مقاله Materials Chemistry
  • ترجمه مقاله Materials Chemistry
  • مقاله شیمی مواد
  • ترجمه مقاله شیمی مواد
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.