Plasmonic silver nanowires for higher efficiency dye-sensitized solar cells

In this article, photovoltaic performance of dye-sensitized solar cells (DSSCs) has been improved by integrating one-dimensional (1-D) plasmonic Ag nanowires into the mesoporous TiO 2 photoanode. We fabricate series of DSSCs by varying the concentrations of Ag nanowires ranging from 0.0 to 1.2 wt.% to evaluate the performance of DSSCs. The localized surface plasmon resonance (LSPR) of Ag nanowires is utilized to enhance light absorption of dye molecules in the mesoporous TiO 2 photoanode. We found that a 0.9 wt.% of Ag nanowires in the TiO 2 photoanode gave an optimum DSSC performance with an enhancement of short circuit current density and power conversion efficiency from 17.14 to 20.30 mA/cm 2 , and 7.57–9.41% respectively as compared to DSSC without Ag nanowires. The enhancement in photovoltaic performance was ascribed to the improvement in light harvesting by LSPR from Ag nanowires.

نانوسیم اکسید کننده نقره برای سلول‌های خورشیدی با خاصیت کارایی بالاتر

در این مقاله، عملکرد سلول‌های خورشیدی رنگدانه ¬ های رنگی (dsscs)با ادغام plasmonic یک بعدی (۱ - D)به درون TiO مزوپور، بهبود یافته‌است. ما با تغییر غلظت‌های نانوسیم‌ها از ۰.۰ تا ۱.۲ wt. درصد برای ارزیابی عملکرد of. برای افزایش جذب نور مولکول‌های رنگی در مزوپور، مورد استفاده قرار می‌گیرد. ما دریافتیم که ۰.۹ wt. % of در the ۲ photoanode در TiO ۲ با افزایش چگالی جریان اتصال کوتاه و بازدهی تبدیل قدرت از ۱۷.۱۴ به ۲۰.۳۰ mA / cm ۲ و ۷.۵۷ - ۹.۴۱ % به ترتیب در مقایسه با DSSC بدون نانوسیم اکسید در مقایسه شدند. افزایش در عملکرد فتوولتائیک به بهبود در برداشت نور توسط lspr از Ag در نظر گرفته شد.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.