Influence of SiCnp content on the microstructure and mechanical properties of ZrB2–SiC nanocomposite

A ZrB2–SiC nanocomposite that introduced nanosized SiC particles into a ZrB2 matrix was fabricated by hot-pressing at 1900 °C for 60 min under a 30 MPa uniaxed load. The composite had an intragranular microstructure that was peculiar to this material. Investigation of the mechanical properties revealed a highest flexural strength of 1009.1 ± 43 MPa and a fracture toughness of 6.8 ± 0.2 MPa m1/2 for the ZrB2–20 vol.% SiC nanocomposite. These improved mechanical properties were strongly dependent on the number of intragranular particles.

تاثیر مقدار SiCnp بر ریزساختار و خواص مکانیکی نانوکامپوزیت ZrB۲ - SiC

ترجمه شده با


پر ارجاع‌ترین مقالات مرتبط:

  • مقاله General Materials Science
  • ترجمه مقاله General Materials Science
  • مقاله علوم مواد عمومی
  • ترجمه مقاله علوم مواد عمومی
  • مقاله Condensed Matter Physics
  • ترجمه مقاله Condensed Matter Physics
  • مقاله فیزیک ماده چگال
  • ترجمه مقاله فیزیک ماده چگال
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.