Alloying-element interactions with austenite/martensite interface during quenching and partitioning of a model Fe-C-Mn-Si alloy

The alloying elements partitioning from martensite to austenite during quenching and partitioning was analysed by coupling in situ High Energy X-Ray Diffraction experiments and 3D atom probe tomography. A rapid and significant carbon partitioning from martensite to austenite without any partitioning of both Mn and Si was highlighted while the interface was immobile. After a relatively short time at 400 °C, a clear Mn partitioning occurs at the vicinity of the α′/γ interface. The analysis conducted indicates that manganese equilibrates its chemical potential during partitioning and raises the issue of the Constrained Carbon Equilibrium model applicability throughout the partitioning process.Graphical abstractDownload : Download high-res image (231KB)Download : Download full-size image

برهمکنش آلمان - فلز با فصل مشترک آستنیت / مارتنزیت در طول جداسازی و تفکیک یک مدل Fe - C - Mn - Si است. scripta Materialia، ۱۶۲، ۱۸۱ - ۱۸۴

ترجمه شده با

پر ارجاع‌ترین مقالات مرتبط:

  • مقاله Condensed Matter Physics
  • ترجمه مقاله Condensed Matter Physics
  • مقاله فیزیک ماده چگال
  • ترجمه مقاله فیزیک ماده چگال
  • مقاله General Materials Science
  • ترجمه مقاله General Materials Science
  • مقاله علوم مواد عمومی
  • ترجمه مقاله علوم مواد عمومی
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.