Effect of anodizing temperature on surface morphology evolution of sputtered hematite films: A potential post-treatment method for further photoelectrochemical performance enhancement

In this study, effect of anodization temperature on the photoelectrochemical (PEC) performance of nanostructured hematite films prepared by anodizing the sputtered iron films on the fluorine-doped SnO 2 glass substrate was investigated. It was noted that increasing the anodization temperature would induce the hematite nanostructure developing from film-like to nanorod morphology. Importantly, this morphology transformation is noted to accompany with the enhanced PEC performance up to 0.59 mA/cm 2 (nanorod structured anodized at 60 °C). Our results clearly demonstrated that the potential of post-treatment using anodization to further enhance the PEC performance of hematite films.

تاثیر دمای anodizing بر روی تکامل مورفولوژی بر روی مورفولوژی فیلم‌های هماتیت: یک روش درمانی بالقوه برای بهبود عملکرد photoelectrochemical.

در این مطالعه، تاثیر دمای anodization بر روی عملکرد photoelectrochemical با ساختار hematite hematite تهیه‌شده با anodizing لایه‌های آهن sputtered بر روی زیرلایه glass doped ۲، مورد بررسی قرار گرفت. لازم به ذکر است که افزایش دمای anodization باعث ایجاد nanostructure hematite در حال توسعه از ساختار لایه به مورفولوژی nanorod می‌شود. به طور مهمی، این تغییر مورفولوژی به همراه افزایش عملکرد PEC به ۰.۵۹ mA / cm ۲ (nanorod structured ساخت یافته در ۶۰ درجه سانتی گراد)نشان‌داده شده‌است. نتایج ما به وضوح نشان داد که پتانسیل تیمار پس از درمان با استفاده از anodization برای افزایش بیشتر عملکرد PEC در فیلم هماتیت می‌باشد.

ترجمه شده با

این مقاله را خودتان با کمک ترجمه کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.