Preparation of M2+/M3+ layered double hydroxides (M2+=Zn, Ni, M3+=Fe): Effect of different M2+ to the layer formation

Two different layered double hydroxides (LDH) materials, namely Ni-Fe LDH and Zn-Fe LDH, have been synthesized by the coprecipitation method under alkaline conditions. The prepared materials were characterized by X-ray diffraction and FT- IR in order to analyze the formation of LDH layer. Although both LDHs contains different M2+ metal, they consist of the same M3+ metal cation, i.e., Fe. Hence, in this work, the effect M2+ metal composition on the formation of LDH layer was investigated. According to the X-ray diffraction analysis, the synthesized ZnFe LDH showed a typical diffraction peak at 2θ of 11.08° with the basal spacing value of 7.98 Å. While for the NiFe LDH exhibited a typical diffraction peak at 2θ around 11.41° with a basal spacing value around 7.74 Å.

آماده‌سازی of + / M۳ + چند لایه‌ای (M۲ + = Zn، Ni، M۳ + = Fe): تاثیر کلاس‌های متفاوت M۲ + به تشکیل لایه

دو ماده لایه‌ای دو لایه‌ای متفاوت (LDH)، یعنی Ni - Fe LDH و Zn - Fe درمحلول، با روش coprecipitation تحت شرایط قلیایی سنتز شدند. مواد تهیه‌شده توسط پراش اشعه ایکس و FT - IR برای تجزیه و تحلیل تشکیل لایه LDH مشخص شد. اگرچه هر دو LDHs دارای انواع مختلف M۲ + فلز متفاوت هستند، اما شامل یک کاتیون metal + و به عنوان مثال، Fe. از این رو، در این اثر، اثر ترکیب فلز روی تشکیل لایه LDH مورد بررسی قرار گرفت. مطابق با آنالیز پراش پرتو ایکس، ZnFe سنتز شده ZnFe سنتز یک پیک پراش را در ۲ θ ۰ ° C با مقدار فاصله‌گذاری اساسی of A نشان داد. در حالی که برای the LDH یک پیک پراش را در ۲ θ در حدود ۱۱.۴۱ ° با مقدار فاصله‌گذاری اساسی حول ۷.۷۴ A به نمایش گذاشت.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.