Solid-solution hardening in dilute and concentrated alloys

Abstract Numerical analysis of the temperature dependence of the critical resolved shear stress of several binary copper-based alloy single crystals containing 0·11 to 7·6 at.% Mn, 0·01 to 14·0 at.% Al, 0·5 to 8·0 at.% Ge and 5 to 30 at.% Zn, has been carried out in terms of the kink-pair formation model of solid-solution hardening. Several solute atoms are found to be involved in the unit activation process not only in concentrated alloys but also in dilute ones. A single mechanism of solution hardening, which involves the interaction between a dislocation and many solute atoms, is therefore operative in all the alloys referred to above.

سخت شدن محلول جامد در آلیاژهای غلیظ و رقیق

چکیده تحلیل عددی وابستگی دمایی تنش برشی حل بحرانی چند آلیاژ دوتایی مبتنی بر مس که شامل ۰. ۱۱ تا ۷. ۶ at. % Mn، ۰. ۰۱ تا ۱۴. ۰ at. % Al، ۰. ۵ تا ۸. ۰ at. % Ge و ۵ تا ۳۰ at. % Zn، بر حسب مدل تشکیل جفت کینک از سخت شوندگی محلول جامد انجام شده‌است. چندین اتم حل‌شده در فرآیند فعال‌سازی واحد نه تنها در آلیاژهای متمرکز بلکه در آلیاژهای رقیق نیز دخیل هستند. بنابراین یک مکانیزم منفرد سخت شدن محلول، که شامل برهم کنش بین یک نابجایی و بسیاری از اتم‌های حل شونده است، در تمام آلیاژهای اشاره‌شده در بالا عمل می‌کند.
ترجمه شده با


پر ارجاع‌ترین مقالات مرتبط:

  • مقاله Condensed Matter Physics
  • ترجمه مقاله Condensed Matter Physics
  • مقاله فیزیک ماده چگال
  • ترجمه مقاله فیزیک ماده چگال
سفارش ترجمه مقاله و کتاب - شروع کنید

با استفاده از افزونه دانلود فایرفاکس چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.