Non-stoichiometry in MgAl2O4 spinel

Stoichiometric magnesium aluminate spinel, MgAl2O4, contains equimolar proportions of Al2O3 and MgO. Spinel can, however, exhibit significant deviations from this stoichiometric composition. There is considerable disagreement concerning which species compensate for either excess Al2O3 or MgO non-stoichiometry. Here, we use empirical and quantum mechanical (density functional theory) atomistic simulation techniques to investigate the defect chemistry accommodating non-stoichiometry. The incorporation of excess Al2O3 was found to be a lower energy process than the solution of excess MgO. Elevated magnesium and aluminium cation vacancy defect concentrations are predicted in Al2O3 rich spinels, whilst MgO excess is facilitated by a combination of oxygen vacancy and magnesium interstitial defects.

در اسپینل MgAl۲O۴

[ ۲ ] آلومینات های منیزیم، اسپینل، MgAl۲O۴، شامل نسبت‌های equimolar Al [ ۲ ] و پشتیبان می‌باشند. با این حال، Spinel می‌توانند انحراف قابل‌توجهی از این ترکیبات استوکیومتری نشان دهند. عدم توافق قابل‌توجهی در رابطه با کدام گونه‌ها برای هر کدام از Al [ ۲ ] و یا پشتیبان غیر - وجود دارد. در اینجا، ما از تکنیک‌های شبیه‌سازی مکانیک کوانتومی و مکانیک کوانتومی (چگالی کارکردی)برای بررسی شیمی عیب accommodating استفاده می‌کنیم. ترکیب Al [ ۲ ] O [ ۲ ] به عنوان یک فرآیند انرژی کم‌تر نسبت به محلول پشتیبان اضافی یافت شد. در Al [ ۲ ] Al [ ۲ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳ ] O [ ۳

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.