Residual stress of composites during curing process in LCM

Liquid composite molding process(LCM)is a widely used manufacturing technique of composite parts. When thermosetting resins are processed, the shrinkage that results from resin polymerization induce the internal stress in the product, which will affect the product quality. Processing induced residual stress of LCM is studied. The FE-analysis was carried out using the computer program ABAQUS. Cure stage analysis is proceeded to obtain a result file of the temperature and the degree of cure fields, which will be set as the start conditions of thermal-stress analysis. And user define material's mechanical behavior (UMAT) subroutine is used to define mechanical properties of the materials as a function of the degree of cure. So the residual stress situation of curing stage is achieved.

تنش باقی مانده کامپوزیت در طول فرآیند درمان در lcm

فرآیند قالب‌گیری ترکیبی مایع (lcm)یک روش تولیدی بسیار پرکاربرد در قطعات کامپوزیتی است. وقتی رزین‌های thermosetting فرآوری می‌شوند، انقباض ناشی از پلیمریزاسیون رزین باعث ایجاد استرس درونی در محصول می‌شود که بر کیفیت محصول تاثیر خواهد گذاشت. پردازش تنش باقی مانده ناشی از lcm مورد مطالعه قرار گرفته‌است. تحلیل آلمان محدود با استفاده از برنامه کامپیوتری ABAQUS انجام شد. آنالیز مرحله درمان به دست آوردن یک پرونده نتیجه از دما و میزان میدان درمان انجام می‌شود که به عنوان شرایط اولیه تحلیل تنش - تنشی تعیین خواهد شد. و کاربر تعریف رفتار مکانیکی material's (umat)را تعریف می‌کند که برای تعریف خواص مکانیکی مواد به عنوان تابعی از درجه درمان استفاده می‌شود. بنابراین، وضعیت استرس باقیمانده مرحله التیام به دست می‌آید.
ترجمه شده با

سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.