Crystallization of Precursors to Forsterite and Chromium-Doped Forsterite

Abstract The pyrolysis and crystallization of poly(methacrylate) precursors and xerogels of forsterite and chromium‐doped forsterite were studied by in situ high‐temperature, dynamic X‐ray diffraction and thermal analysis. For both types of precursor, crystallization of forsterite occurred at lower temperature when doped with chromium. Also, exotherms above 700°C occurred 50°C lower when chromium was present. When residual carbon in the xerogels was more than ∼1%, an unidentified crystalline intermediate phase formed at ∼800°C. Conversion of the intermediate phase to forsterite was faster than amorphous material. Thus, full crystallinity was attained at a lower temperature when the xerogels had some residual carbon.

Crystallization of به کروم و کروم - doped Forsterite

چکیده The و crystallization مواد اولیه پلی (methacrylate)و xerogels of و chromium - با دمای بالا، پراش اشعه ایکس و آنالیز حرارتی مورد مطالعه قرار گرفتند. برای هر دو نوع of، تبلور of در دمای کم‌تر هنگامی رخ داد که با کروم تولید شده بود. هم چنین، بالای ۷۰۰ درجه سانتی گراد زمانی که کروم موجود بود به ۵۰ درجه سانتی گراد رسید. هنگامی که کربن باقیمانده در xerogels بیش از ۱ % بود، یک فاز میانی میانی که در دمای ۸۰۰ درجه سانتی گراد ایجاد شد. تبدیل مرحله میانی به forsterite سریع‌تر از مواد آمورف بود. از این رو، بلور کامل در دمای پایین‌تر هنگامی که the مقداری کربن باقی مانده داشت به دست آمد.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.