Modification of MgAl2O4 Microwave Dielectric Ceramics by Zn Substitution

Abstract MgAl2O4 microwave dielectric ceramics were modified by Zn substitution for Mg, and their dielectric characteristics were evaluated, along with their structures. Dense (Mg1−x Znx )Al2O4 ceramics were obtained by sintering at 1550°–1650°C in air for 3 h, and the (Mg1−x Znx )Al2O4 solid solution was determined in the entire composition range. With Zn substitution for Mg, the dielectric constant ɛ of MgAl2O4 just varied from 7.90 to 8.56, while the Q ×f value had significantly improved up to a maximal value of 106 000 GHz at x =1.0. Moreover, the τf of MgAl2O4 ceramics had declined from −73 to −63 ppm/°C.

اصلاح of MgAl۲O۴ ماده دی‌الکتریک با جانشینی Zn (Zn)

چکیده سرامیک عایقی microwave با جانشینی Zn برای منیزیم اصلاح شد و خصوصیات دی‌الکتریک آن‌ها به همراه ساختار آن‌ها مورد ارزیابی قرار گرفت. سرامیک‌های پرپشت (Mg۱ - x Znx)با sintering در دمای ۱۵۵۰ ° C ° C به مدت ۳ ساعت به دست آمدند و محلول جامد (Mg۱ - x Znx)در کل محدوده ترکیب‌بندی تعیین شد. با جانشینی Zn برای منیزیم، ضریب دی‌الکتریک ثابت MgAl۲O۴ از ۷.۹۰ تا ۸.۵۶ متغیر بود، در حالی که مقدار Q * f به طور قابل‌توجهی در مقدار حداکثر ۱۰۶ GHz در x = ۱.۰. تغییر کرده بود.
ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.