Forming Limit Diagram of Magnesium Alloy ZK60 at Elevated Temperature

<jats:p>The forming limit diagram of magnesium alloy ZK60 was developed with Hill’s instability criterion and M-K analysis. The relationship of forming limit with stain path, temperature and the thickness irregular coefficient were analyzed. The results show that the forming limit of ZK60 magnesium alloy increased little with the rising of strain ratio, but influenced greatly by the failure definition , and forming limit of is increased with the rising of temperature and thickness irregular coefficient, the most suitable value of f0 is 0.99, the fracture occur on the grain boundaries with significant cavities formation.</jats:p>

تشکیل نمودار محدود منیزیم Alloy در دمای Elevated

< jats: صفحه تشکیل شکل تشکیل آلیاژ منیزیم با معیار ناپایداری تپه و آنالیز M - K ایجاد شد. رابطه بین حد شکل‌گیری با مسیر لکه، دما و ضریب نامنظم ضخامت بررسی شد. نتایج نشان می‌دهد که حد تشکیل آلیاژ منیزیم ZK۶۰ با افزایش نسبت کشش افزایش می‌یابد، اما تحت‌تاثیر تعریف شکست قرار می‌گیرد و حد شکل‌گیری با افزایش دما و ضریب نامنظم افزایش می‌یابد، مطلوب‌ترین مقدار of، ۰.۹۹ است، که شکستگی در مرزه‌ای دانه با تشکیل حفرات قابل‌توجه رخ می‌دهد. < / jats: p >

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.