Microstructure and Residual Stress in Rotary Friction Welded Dissimilar Metals of AA7020 Aluminium Alloy with 316L Steel

Rotary friction welding (RFW) was used in the current study to join the dissimilar metals AA7020-T6 aluminium alloy and 316L steel. Neutron diffraction was performed to investigate the texture gradient around the weld line and to map the residual stress over the whole specimen. The texture analysis showed a weak shear component near the bond line of AA7020-T6-T6 side which indicated a plastic deformation of AA7020-T6 during welding. The shear bands were also observed in optical microstructures. Relatively high tensile residual stresses were observed near the bond line on the AA7020-T6 side, which were in-homogeneously distributed from the perimeter to the rod centre, while high compressive residual stresses were found in the sample centre at the bond line in the 316L steel.

استرس Microstructure و Residual در اصطکاک روتاری: فلزات آهنی آلیاژ آلومینیوم AA۷۰۲۰ با فولاد ۳۱۶ آل.

از جوشکاری اصطکاکی روتاری (rfw)در مطالعه حاضر برای پیوستن به فلز dissimilar AA۷۰۲۰ - T۶ آلومینیوم و فولاد ۳۱۶ آل استفاده شد. پراش نوترون برای بررسی گرادیان بافت اطراف خط جوش و برای نقشه تنش پسماند در کل نمونه انجام شد. آنالیز بافت یک مولفه برشی ضعیف در نزدیکی خط پیوند of - T۶ - T۶ نشان داد که تغییر شکل پلاستیک of - T۶ در حین جوشکاری را نشان داد. باندهای برشی نیز در microstructures نوری مشاهده شدند. تنش‌های پسماند کششی نسبتا بالا نزدیک خط پیوند در سمت AA۷۰۲۰ - T۶ مشاهده شد که به طور یکنواخت از محیط به مرکز میله‌ای توزیع شده‌بودند در حالی که تنش‌های پسماند فشاری بالا در مرکز نمونه در خط پیوند در فولاد ۳۱۶ آل یافت شد.

ترجمه شده با

Download PDF سفارش ترجمه این مقاله این مقاله را خودتان با کمک ترجمه کنید
سفارش ترجمه مقاله و کتاب - شروع کنید

95/12/18 - با استفاده از افزونه دانلود فایرفاکس و کروم٬ چکیده مقالات به صورت خودکار تشخیص داده شده و دکمه دانلود فری‌پیپر در صفحه چکیده نمایش داده می شود.